Classifications
Characteristics
Suitable for welding AISI 302,304,304L austenitic stainless steels, providing good corrosion, excellent toughness at cryogenic temperature.
Applications
Ideal for steels of AISI 302, 304, 304, 304L,308, 308L used in dairy, food processing units, pharamaceutical and chemical industries.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.04 max |
| Mn |
1.00 - 2.40 |
| Si |
0.65 max |
| Ni |
9.00 - 10.00 |
| Cr |
18.00 - 22.00 |
| Mo |
0.60 - 0.75 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
Charpy Impact Value at -196°C |
| 590 - 650 MPa |
420 - 450 MPa |
40 - 50 |
75 - 85 J |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
Stainless Steel filler wire containing higher Chromium & nickel , suitable for joining materials of similar composition and also dissimilar stainless steels.
Applications
For welding of AISI 309 stainless steel, straight chrome steels, 18/8 clad steels, low alloy and carbon steel overlaying of ss weld metal on ferritic steel.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.04 max |
| Mn |
1.00 - 1.40 |
| Si |
0.45 max |
| Ni |
12.00-13.00 |
| Cr |
23.00-25.00 |
| Mo |
0.60 - 0.75 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
Charpy Impact Value at 0°C |
| 530 - 600 MPa |
400 - 430 MPa |
30 - 35 |
110 J |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
25/20 type Stainless Steel filler wire with low carbon suitable for heat resistant , austenitic stainless steels, where application is subject to high temperatures.
Applications
Suitable for welding of AISI 310 grade plates, German steel grades 4762, 4828, 4841, 4846 & 4848, straight chromium steel, dissimilar steels, high temperature furnace parts annealing boxes etc.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.02 max |
| Mn |
1.30 - 1.60 |
| Si |
0.45 max |
| Ni |
20.00 - 22.00 |
| Cr |
25.00 - 28.00 |
| Mo |
0.60 - 0.70 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
Charpy Impact Value at -196°C |
| 590 - 650 MPa |
420 - 450 MPa |
40 - 50 |
75 - 85 J |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
Stainless Steel filler wire suitable for welding cast alloys of similar composition, dissimilar steels and steels of unknown composition.
Applications
Welding and surfacing of tool steel, spring steel, case hardening steel manganese steel, heavy machine parts and earth moving equipment parts, dissimilar joints between stainless and carbon steels etc.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.10 max |
| Mn |
1.30 - 1.60 |
| Si |
0.45 max |
| Ni |
8.00 - 10.00 |
| Cr |
28.00 - 32.00 |
| Mo |
0.60 - 0.70 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
| 640-820 MPa |
500 - 520 MPa |
21 - 23 |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
A molybdenum bearing Stainless Steel filter wire with low carbon content. It is corrosion resistant and suitable for welding molybdenum bearing stainless steels.
Applications
Suitable for AISI 316L, 317 L grade stainless steel used in chemical plants, paper industries, textile industries etc.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.02 max |
| Mn |
1.30 - 2.00 |
| Si |
0.45 max |
| Ni |
11.00 - 13.00 |
| Cr |
17.00 - 20.00 |
| Mo |
2.00 - 3.00 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
Charpy Impact Value at -196°C |
| 530 - 570 MPa |
370 - 420 MPa |
35 - 45 |
45 - 55 J |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
Stainless Steel filler wire, Cg stabilized to prevent weld decay, giving excellent corrosion resistance, suitable for use on Cbor Ti stabilized 18/8 Mo steels such as 317 and 318 and when the weld is subjected to temperature more than 800° C.
Applications
Suitable for bleaching, dyeing equipments and pickling plants.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.02 max |
| Mn |
1.30 - 2.25 |
| Si |
0.45 max |
| Ni |
13.00 - 14.00 |
| Cr |
18.00 - 19.00 |
| Mo |
2.00 - 3.00 |
| Cb |
0.60-0.70 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
| 520 - 570 MPa |
380 - 420 MPa |
20 - 27 |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
Stainless Steel filler wire , niobium to prevent weld decay, giving excellent corrosion resistance. Suitable for use on 18/8 type stainless steel, Nb and Ti stabilized, such as 304, 32.1 and where the weld is subjected to temperatures above 400° C.
Applications
Suitable for aircraft fabrication, stainless steel pipelines, tanks, fittings and hospital equipment.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.07 max |
| Mn |
1.00 - 2.50 |
| Si |
0.45 max |
| Ni |
9.00 - 11.00 |
| Cr |
17.00 - 21.00 |
| Nb |
0.50 - 0.60 |
| Mo |
0.50-0.75 |
| Cu |
0.75 Max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
| 600 - 650 MPa |
450 - 500 MPa |
35 - 40 |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C
Classifications
Characteristics
Suitable for AISI 430 stainless steel where maximum corrosion resistance up to 1600o required.
Typical Weld Metal Composition
|
Element
|
Percentage
|
| C |
0.15 max |
| Mn |
0.50-0.60 |
| Si |
0.45 max |
| Ni |
0.50-0.60 |
| Cr |
16.00-17.00 |
| Mo |
0.60-0.70 |
| Cu |
0.75 max |
| P |
0.03 max |
| S |
0.03 max |
Typical Mechanical Properties of all Weld Metal
| Tensile Strength |
Yield Strength |
Elongation % (L=4d) |
| 520 - 570 MPa |
380 - 420 MPa |
22-27 |
Current Range & Packing Data
| Size |
Wire ( Plastic Spool ) |
Rods (1000 mm Length) |
| 0.8mm |
15 Kg |
5 Kg |
| 1.2mm |
15 Kg |
5 Kg |
- Hardness: 180 BHN
- Melting Point: 1440°C